Ceramic random heaping tower packing |
|
Product Name:
|
Ceramic random heaping tower packing |
|
Description:
|
Chemical composition and physical properties :
Al2O3: 23% ;
Specific gravity T/m3: 2.2 ;
SiO2: 69.5% ;
Acid resistance % : 99.8 ;
MgO : 0.45% ;
Alkaline resistance % : 96 ;
Fe2O3: 0.5% ;
Compressive strength kg/cm2: 4800 ;
Ca0 : 0.5% ;
Bend strength kg/cm2: 700 ;
Na20 : 0.36% ;
Water absorption % : < 1 ;
K20 : 1.3% ;
Hardness Mohs : 7 ;
Burning lost : 4.1% ;
hot stability 200-15degree : Do not split three times .
Some of the feature and parameter are given to you for a reference as follows:
Name :Rasching ring ;
Specification mm :25;
Dimension d×h?#948;:25?5?.5 ;
Specific surface area m2/m3 :235;
Void rate m3/m3:0.78 ;
Num N/m3:49000;
Heaping Weight kg/m3:560;
Dry packing Factor m-1:784 .
Name :Rectangle saddle ring ;
Specification mm :25;
Dimension d×h?#948;:25?0? ;
Specific surface area m2/m3 :200;
Void rate m3/m3:0.77 ;
Num N/m3: 58230 ;
Heaping Weight kg/m3:560;
Dry packing Factor m-1:434.
Name :Different saddle ring ;
Specification mm :25;
Dimension d×h?#948;:25?0? ;
Specific surface area m2/m3:216;
Void rate m3/m3:0.78 ;
Num N/m3:58300 ;
Heaping Weight kg/m3:530;
Dry packing Factor m-1:340
There are different technical datas of other types and further more informations of each type can be read on our website .
|
|
Features:
|
Ceramic random heaping tower packing has excellent heat and acid resistance,and it can bear the corrosion of various inorganic acid,organic acid and organic solvent except hydrofluoric acid.The product can be used on diversified occasion in high temperature,low temperature and high strength corrosion,therefore has a wide application.It is able to be applied in the drying tower,absorbing tower,cooling tower,washing tower,regenerative tower and desulfurization tower in chemical engineering,metallurgy,coal gas,acid and oxygen production,pharmacy and other industries.
|
|
|
|
|
|
|
 |